Chemical nature of the anion antisite in dilute phosphide GaAs1−xPx alloy grown at low temperature

Résumé

While nonstoichiometric binary III-V compounds are known to contain group-V antisites, the growth of ternary alloys consisting of two group-V elements might give additional degrees of freedom in the chemical nature of these antisites. Using cross-sectional scanning tunneling microscopy (STM), we investigate low-temperature-grown dilute GaAs1−xPx alloys. High concentrations of negatively charged point defects are found. Combined with transmission electron microscopy and pump-probe transient reflectivity, this study shows that the defects have a behavior similar to the group-V antisites. Further analyses with x-ray diffraction point to the preferential incorporation of arsenic antisites, consistent with ab initio calculations, that yield a formation energy 0.83 eV lower than for phosphorus antisites. Although the negative charge carried by the arsenic antisites in the STM images is shown to be induced by the proximity of the STM tip, the arsenic antisites are not randomly distributed in the alloy, providing insight into the evolution of their charge state during the growth.
Fichier principal
Vignette du fichier
PRM2p104601_2018_HAL.pdf (1.79 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01912292 , version 1 (12-11-2018)

Identifiants

Citer

T. Demonchaux, K. K. Sossoe, M. M. Dzagli, J. P. Nys, Maxime Berthe, et al.. Chemical nature of the anion antisite in dilute phosphide GaAs1−xPx alloy grown at low temperature. Physical Review Materials, 2018, 2 (10), pp.104601. ⟨10.1103/PhysRevMaterials.2.104601⟩. ⟨hal-01912292⟩
144 Consultations
135 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More