Bond strength and interfacial morphology of orthodontic brackets bonded to eroded enamel treated with calcium silicate–sodium phosphate salts or resin infiltration - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Angle Orthodontist Année : 2016

Bond strength and interfacial morphology of orthodontic brackets bonded to eroded enamel treated with calcium silicate–sodium phosphate salts or resin infiltration

Résumé

Objective: To investigate the shear bond strength (SBS) of orthodontic brackets bonded to eroded enamel treated with preventive approaches and to examine the enamel/bracket interfaces. Materials and Methods: Ninety-one brackets were bonded to seven groups of enamel samples: sound; eroded; eroded+treated with calcium silicate–sodium phosphate salts (CSP); eroded+infiltrated by ICON®; eroded+infiltrated by ICON® and brackets bonded with 1-month delay; eroded+infiltrated by an experimental resin; and eroded+infiltrated by an experimental resin and brackets bonded with 1-month delay. For each group, 12 samples were tested in SBS and bond failure was assessed with the adhesive remnant index (ARI); one sample was examined using scanning electron microscopy (SEM). Results: Samples treated with CSP or infiltration showed no significant differences in SBS values with sound samples. Infiltrated samples followed by a delayed bonding showed lower SBS values. All of the values remained acceptable. The ARI scores were significantly higher for sound enamel, eroded, and treated with CSP groups than for all infiltrated samples. SEM examinations corroborated the findings. Conclusions: Using CSP or resin infiltration before orthodontic bonding does not jeopardize the bonding quality. The orthodontic bonding should be performed shortly after the resin infiltration.

Mots clés

Fichier principal
Vignette du fichier
Costenoble2016.pdf (1.2 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02511428 , version 1 (18-03-2020)

Identifiants

Citer

Aline Costenoble, Elsa Vennat, Jean-Pierre Attal, Elisabeth Dursun. Bond strength and interfacial morphology of orthodontic brackets bonded to eroded enamel treated with calcium silicate–sodium phosphate salts or resin infiltration. Angle Orthodontist, 2016, 86 (6), pp.909-916. ⟨10.2319/111315-764.1⟩. ⟨hal-02511428⟩
259 Consultations
49 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More